Teknopoliderz Two Component Joint Filler

Product description
It is a two component, self leveling, bitumen modified polyurethane based joint filler and waterproofing mastic. It is used in building and ground joints. It is resistant to vehicle traffic.

Usage areas
• On concrete, surface hardener, asphalt, natural stone, mosaic and sheet metal surfaces with appropriate primer,
• In building dilatations,
• Thanks to its chemical resistance, it is ideal for areas under the influence of chemicals.
• It can be easily applied in electrical cable joints.
• On floors under the influence of oil and fuel,
• Refineries, Gas stations, fuel centers,
• Military areas,
• Industrial areas, floor joints of warehouses,
• Floor joints in parking lots and garages,
• In the joints of asphalt and concrete roads and repair of cracks, joint joints,
• It is manufactured to be used in horizontal applications.

Features and Advantages
• High self-adjustment feature (si-type).
• It has high resistance against de-icing chemicals.
• It is polyurethane based.
• Solvent free.
• It is cold applied.
• Self-leveling, can be applied by hand pouring or with a joint machine.
• Tix is ​​used for vertical applications.
• Resistant to oils and many chemicals.
• Its flexibility does not deteriorate in different air temperatures.
• Resistant to rot and plant roots.

Application Instructions
Joint Preparation: The width of the joints should not be less than 6 mm. Grouting depth up to 6 mm wide should be equal to the width. For joints with a width of 10 - 30 mm, the filling depth should be half the width. For even wider joints, the filling depth should be at least half the width. In order to adjust the depths in question, base material (wick, sandblasting, etc.) should be used in the joint.

Surface Quality: Surfaces must be clean, smooth, solid and dry, weak parts must be removed from the surface. Do not apply on damp surfaces.

Surface Preparation: Joints should be thoroughly cleaned with a wire brush, spiral or sandblasting prior to application, and dust should be cleared by blowing air into the joint space.
Masking tape is adhered to the upper parts of the joints, not to the middle. This application must be done in order to prevent the mastic from spreading around and to ensure that it comes out properly. It is used with a cartridge/ sausage gun/ mouth-loading gun to press the sealant into the joint. It is mixed with a low-speed mixer in the Teknopoliderz 2K package and placed inside the sausage gun. The tip of the cannula is adjusted according to the joint opening to be applied. By pressing the sausage gun trigger, the polyurethane sealant is pushed forward.

3-5 minutes after the mastic hardens, the gloved index finger is dipped in the soap bar. Afterwards, it is ensured that the surface is smoothed by back and forth movements on the applied mastic. After this process is completed, the masking tape is removed and thrown away.

Curing Stage: Components A and B should be applied within an average of 35 minutes after mixing. The product gets hand-dry within 24 hours, mechanical strength within 48 hours, and full strength within 7 days.

Application Notes / Limitations
• All mastication processes should be done at temperatures above (+)5 °C. Because the moisture on the surface affects the adhesion negatively.
• TEKNOBOND 110 should be applied as a primer on the joint cheeks.
• The surfaces on which TEKNOPOLIDERZ TWO COMPONENT will be applied must be absolutely dry, free from moisture and dirt.
• Drying time, different surfaces and air temperatures may affect usage and drying times.
• Values ​​are given for (+)20 °C desired temperature environment. High temperatures shorten the time, low temperatures lengthen the time.
• Sausage gun, soap bar, masking tape, scissors or utility knife can be used in the application.
• After the application, it should be protected against adverse weather conditions such as direct sunlight, strong wind, high air temperature (over +50 °C), rain and frost.
• Equipment should be cleaned with TEKNOTINER immediately after the application, before it hardens.